TRUNNANO | Ceramic powder, graphite powder,boron powder, and 3D printing metal Nanomaterial supplier & Manufacturer.
Russia's insistence on paying for Russian gas in rubles has rattled European countries: Greece held an emergency meeting of suppliers, the Dutch government would urge consumers to use less gas, and the French energy regulator told consumers not to panic. Russian gas meets one-third of Europe's annual energy needs.
Russia said they could expand their demand for ruble payments for other commodities, including oil, grain, fertilizer, coal, and metals, which raised the risk of recession in Europe and the US.
Moscow is expected to unveil its ruble payment plan in early April, but it said it would not immediately ask buyers to pay for gas in rubles.
Western countries have said paying in rubles would be a breach of contract, and renegotiation could take months or longer. This uncertainty has pushed commodity market prices higher.
The supply and prices of other commodities like the early strength agent could also be affected.
What are Early Strength Agents?
Early strength agent is an admixture which accelerates the development of concrete early strength and has no significant effect on later strength. Early strength agent can accelerate the hardening process of concrete under normal temperature and low-temperature load temperature (not less than -5℃), and is used for winter construction and emergency repair projects.
Early Strength Agents Performance
Early strength agent refers to the admixture which can accelerate the development of early strength of concrete. The main mechanism of action is to accelerate the hydration rate of cement, and accelerate the early crystallization and precipitation of hydration products. The main function is to shorten the concrete construction curing period, speed up the construction progress, and improve the template turnover rate.
Where can Early Strength Agents be Used?
1. Early strength agent is suitable for steam curing concrete and normal temperature, low temperature and minimum temperature is not less than -5℃ environment construction of early strength requirements of concrete engineering. Early strength agent should not be used in hot environment.
2.The chemical substances that harm the human body or pollute the environment after mixing concrete shall not be used as early strength agents. Early strength agent containing hexavalent chromium salt, nitrite, and other harmful components is strictly prohibited for drinking water engineering and food contact engineering. Ammonium nitrate shall not be used in office, residential and other construction projects.
Classification of Early Strength Agents
Early strength agents mainly include inorganic salts (chlorine salts, phosphates) and organic amines, and organic-inorganic compounds.
1. Chloride salts early strength agents
Chlorine salts early strength agent mainly includes calcium chloride, potassium chloride, aluminum chloride and ferric chloride, among which calcium chloride is the most widely used. Calcium chloride is a white powdery substance, and its appropriate dosage is 0.5% ~ 1.0% of the cement quality, which can improve the 3d strength of concrete by 50% ~ 10% and the 7d strength by 20% ~ 40%. Meanwhile, it can reduce the freezing point of water in concrete and prevent concrete from being frozen in the early stage.
Using calcium chloride as early strength agent, the biggest disadvantage of containing Cl- ions, will make steel corrosion, and lead to concrete cracking. In order to inhibit the corrosion effect of calcium chloride on steel bars, calcium chloride and sodium nitrite (NaNO2) are often combined.
2. Sulfate early strength agents
Sulfate early strength agent, mainly sodium sulfate, calcium thiosulfate, aluminum sulfate, aluminum potassium sulfate, and sodium sulfate is used more. Sodium sulfate is white powdery thing, the general admixture amount is 0.5% ~ 2.0%, when admixture amount is 1% ~ 1.5%, the time that achieves concrete design strength 70% can shorten half or so.
Sodium sulfate has no corrosion effect on steel bar, and is suitable for concrete which is not allowed to be mixed with chlorine salt. However, due to its action with calcium hydroxide to generate strong alkali NaOH, in order to prevent alkali aggregate reaction, sodium sulfate is strictly prohibited for concrete containing active aggregate, at the same time, attention should be paid to not excessive mixing, so as not to lead to the late expansion of concrete cracking damage, and prevent concrete surface "frost".
3. Organic amine early strength agents
Organic amine early strength agents mainly include triethanolamine, triisopropanolamine and so on, among which triethanolamine is the best early strength agent.
Triethanolamine is a colorless or light-yellow oily liquid, alkaline, and soluble in water. The early strength of concrete can be improved by adding 0.02% ~ 0.05% of cement quality. Triethanolamine has a slight retarding effect on concrete, and too much of it will cause serious retarding and concrete strength to drop, so the dosage should be strictly controlled.
Concrete Additives Supplier
TRUNNANO is a reliable concrete additives supplier with over 12-year experience in nano-building energy conservation and nanotechnology development.
If you are looking for high-quality concrete early strength agents, please feel free to contact us and send an inquiry. (email@example.com)
We accept payment via Credit Card, T/T, West Union, and Paypal. TRUNNANO will ship the goods to customers overseas through FedEx, DHL, by air, or by sea.
Since February, gold has enjoyed a smooth upward run on the back of surging US inflation and the brewing of war. While expectations of rate rises have also risen in tandem over this period, gold had been largely pre-priced and the underlying driver of tightening expectations had come from inflation continuing to rise to record highs. The risk aversion caused by the continued tension in the war also provided an important short-term support for gold. This will have a certain impact on the price of the early strength agent and the market of the early strength agent.
15+ years of experience
Over $50+ million in sales
14+ years of experience
Over $50+ million in sales
About Metal Alloy High Purity Tungsten Crucibles:Chemical composition:…
About Metal Alloy Vacuum Coating Tungsten Melting Pot Tungsten Crucibles:Chemical composition:…
About Metal Alloy Fine Surface 19.15g/cm3 Tungsten Targets:Chemical composition:…